| 原産地: | 中国(本土) | 銘柄: | clayde | モデル番号: | zl10221 | アプリケーション: | セラミック構造 | モデル番号: | 0.2~60mm | ブランド名: | clayde | applications1: | despersingと極細研削塗料、 顔料、 コーティング、 インク | applications2: | Eelectronic材料、 の磁気バンド、 ナノ- 材料、 mlcc | applications3: | 化学fibe用酸化チタン、 セラミック釉薬 | applications4: | 薬、 化粧品など | 充填密度: | 3.6~3.8g/cm3 | 特定の密度: | 6.0g/cm3 | 曲げ強度: | â¥1000mpa |
包装
| 包装: | 25kg/drum |
94.5%ZrO2 5.25% Y2O3 zirconic ceramic beads
The zirconia grinding medium was made by high quality raw material and advanced processing technic. It can be used by sand mill, grinder, agitatorglobe mill, roller globe mill to made efficient, clean and economical dispersion and grinding to electronic pastes, ceramic powder, magnetic material, cell raw material, rare earth material, non-metallic ore, oil based paint, paint, printing ink, ink paint, coarse whiting, titanium pigment, farm chemical and some raw materials of food and medicine.
Compared with the traditional grinding medium such as alumina balls, zirconium silicate balls, steel balls, agate balls and glass pearls, the zirconia grinding mediumY-TZP grinding mediumhas high density, high hardness and high tenacity features, which provide it higher grinding efficiency than the traditional grinding medium.
High-wearing zirconia grinding medium can protect materiels from pollution and guard against chemical corrosion to shorten the useful time of grinding medium.
Material Properties Of TZP
Composition | wt% | 94.5% ZrO2,5.5%Y2O3 |
Specific density | g/cm3 | ≥6.0 |
Hardness(HV) | HRA | >10 |
Thermal expansion | X10-6/K | 11 |
Coefficient(20400) | ||
Elastic modulis | GPa | 205 |
Fracture toughness | Mpa·m1/2 | 7-10 |
Bending strength | MPa | 1150 |
Grain size | Um | <0.5 |
Thermal conductivity | w/(m·k) | 3 |
CHINA CHANGSHA ZHonGLONG CHEMICAL CO.,LTD
LANEY LEI
0086-15387539183
ANY QUESTION,PLS LET US KNOW!