Machinery yttria-stabilized zirconia pump ceramic shaft.
Material: zirconia ceramic
high Density: above 6.0 g/cm3.
Specification:OD3*10mm.
Advantage of zirconia Pump ceramic shaft.
1,high mechanical strength
2,high temperature, Max working temperature: 1100C.
3,good electrical insulation
4,Good chemical corrosion resistance under high temperature.
5,Excellent wear and abrasion resistance
6,Very hardness and Excellent thermal shock
Zirconia Pump ceramic shaft application.
Zirconia Pump ceramic shaft has strong resistance to the high temperature and high pressure, lower ratio of the moisture absorption, stable chemical properties, and its capacity of enduring the corrosion of acid, alkali, and organic solvent make it widely utilized in Petroleum exploration, Mechanical industry, chemical industry, natural gas, Medical equipment and environmental protection fields etc.
Zirconia ceramic shaft widely used in Health care,blood dialysis machine, pump, ultrafiltration pump, High pressure washing machine, Oil well drilling equipment, mud pump Electronic insulator etc
Zirconium Oxide ceramics form Method including: dry press forming, isostatic pressing molding, grouting, hot die-casting molding, cast molding, injection molding, plastic extrusion, colloidal forming of solidification etc. The most widely used form methods are injection molding and dry pressing.
Zirconia ceramic material has the advantage of high toughness and high bending strength, good thermal expansion coefficient, high impact resistant, Its superior performance close to the advantages of steel. So it widely used in electronics, machinery, aerospace, petrochemical and other fields.
Property | Density | g/cm3 | 6 |
Sintering Temperature | 1600 | ||
Weibull Modulus | m | 23 | |
Vickers Hardness | HV0.5 | 1300 | |
Flexural Strength | Mpa | 1000 | |
Thermal Performance | Thermal Expansion | X10-6/K | 10 |
Heat Resistance Impact Force | T() | 360 | |
Thermal Conductivity | W/mk | <2 | |
Thermal Shock Resistance | ΔT | 270 | |
Highest Application Temperature | 1000 | ||
Physical Properties
| Compressive Strength | Mpa | 3000 |
Fracture Toughness | Map.m3/2 | 6-8 | |
Modulus Of Elasticity | GPa | 200 | |
Impact Resistance | MPa.m1/2 | 8 | |
Electrical Characteristics | Volume Resistivity at 20 | Ωcm | >10^12 |
Dielectric breakdown strength | KV/mm | - | |
Dielectric constant | 100MHz(E) | - | |
1 MHZ dielectric loss Angle at 20 |
tanδ | - |
Choose Seamark Ceramic, we are now able to offer following services:
1. Before sales service: we will reply all your questions or inquiry in time, if you need some suggestion on your project, it will be our pleasure to do it.
2. In contract: our strict quality control is performed in every step of producing; we pay attention on every detail to ensure you are satisfied with our products and service.
3. After sales service: any questions, please let us know by email or phone, we will help you to deal with those problems.
If you need any further information, please do not hesitate to contact us.