原産地: 中国(本土) | 銘柄: TK | 材料: clay bricks |
タイプ: caly bricks |
| |
AI2O3(%) | 30 |
Fe2O3 (%) | 3 |
Refractoriness (SK) | 32 |
Refractoriness under load, 0.2MPa, Ta, ((°C) | 1300 |
Porosity (%) | 22-26 |
Bulk density (g/cm³) | 2.05 |
Cold crushing strength (MPa) | 25 |
Thermal expansion at 1000°C (%) | 0.6 |
|
|
| |
AI2O3(%) | 38 |
Fe2O3 (%) | 2.5 |
Refractoriness (SK) | 34 |
Refractoriness under load, 0.2MPa, Ta, ((°C) | 1350 |
Porosity (% | 19-23 |
Bulk density (g/cm³) | 2.10-2.15 |
Cold crushing strength (MPa) | 25 |
Thermal expansion at 1000°C (%) | 0.6 |
|
|
| |
AI2O3(%) | 50 |
Fe2O3 (%) | 2 |
Refractoriness (SK) | 36 |
Refractoriness under load, 0.2MPa, Ta, ((°C) | 1450 |
Porosity (% | 20-24 |
Bulk density (g/cm³) | 2.30-2.40 |
Cold crushing strength (MPa) | 45 |
Thermal expansion at 1000°C (%) |