製品情報
原産地: 中国(本土) | タイプ: セラミック・チューブ | 適用: 耐火物 |
材料: 陶磁器アルミナ | モデル番号: AV-alumina ceramic tube | 銘柄: AV |
包装
包装: Standrad export pcking |
仕様
99% AL2O3 ceramic tube 1.Processed by hot-pressing 2.No pollution 3.Superior performance
Wholesale customize 99% AL2O3 ceramic tube
ng>Productive Technology: ng>
ng> ng>Wearable ceramic is the special corundum ceramic that has been sintered under 1800°C with the main raw material of Al2O3 and flux of rare metal oxide.
Using the high strength organic/inorganic bond to felt together,
and then grinding to the size as drawing required.
1.Heat-resistant
2.Good insulation
3.High strength
4.Precision Process
5.Wear-resistant
Alumina Ceramics Properties | |||
Unit | 95% | 99% | |
Density | g/cm3 | 3.6 | 3.8 |
Water absorption | % | <0.4 | <0.2 |
Firing temperature | °C | 1600 | 1800 |
Hardness | HRA | 70 | 80 |
Coefficient of linear expansion | *10-6/°C | 5.5 | 5.3 |
Dielectric constant | 9 | 10.5 | |
Volume resistivity | Ω·cm | — | 1013 |
Breakdown voltage | KV/mm | 14 | 15 |
Breaking strength | Mpa | 250 | 300 |
Bulk Density | g/cm3 | ≥3.6 | ≥3.7 | ≥5.8 | ≥3.2 | |
Acid Resistance | 1:9HCl | mg/cm2 | ≤7 | ≤0.7 | ||
Alkali Resistance | 10% NaOH | mg/cm2 | ≤0.2 | ≤0.1 | ||
Tensile Strength | 25°C | Mpa | ≥160 | ≥190 | ≥320 | |
Flexural Strength | 25°C | Mpa | ≥280 | ≥300 | ≥1000 | ≥700 |
Thermal Shock Resistance | The sample in 800±10°C heating furnace heat preservation 30 minutes, removed in a asbestos board, naturally cooled to room temperature, repeat 10 times, no crack and burst phenomenon. | |||||
Coefficient of Linear Expansion | 20-500°C | 1X 10-6/°C | 6.5-7.5 | 6.5-7.5 | 9.5-10.5 | 3.1-3.3 |
20-800°C | 1X 10-6/°C | 6.5-8.5 | 6.5-8.5 | 9.5-10.5 | 3.1-3.3 | |
Young's Modulus of Elasticity | Gpa | ≥280 | ≥280 | ≥210 | ≥300 | |
Dielectric Loss | 1MHz 20°C | 1X 10-4 | ≤4 | ≤2.5 | ||
Dielectric Constan | 1MHz 20°C | 9-10 | 9-10.5 | |||
Volume Resistivity | 100°C | Ωcm | ≥1013 | ≥1013 | ||
300°C | Ωcm | ≥1010 | ≥1010 | ≥1010 | ≥1018 | |
500°C | Ωcm | ≥108 | ≥109 | |||
Dc Breakdown Strength | D.C. | Kv/mm | ≥18 | ≥15 | ||
Vickers Hardness | Mpa | 1600 | 1650 | 1200 | 1600 | |
Fracture Toughness | MPam½ | 3.8 | 4.2 | 10 | 7 | |
Poisson's Ratio | 0.22 | 0.25 | 0.3 | 0.25 |