工業的用途のためのASTM B348 GR5チタンバー
1.Chemical composition
Grade | Ti | Chemical composition | ||||||||||||
Major composition | residual elements(not more than) | |||||||||||||
Al | V | Sn | Mo | Pa | Fe | C | N | H | O | |||||
Gr1 | Bal | / | / | / | / | / | 0.20 | 0.08 | 0.03 | 0.015 | 0.18 | |||
Gr2 | Bal | / | / | / | / | / | 0.30 | 0.08 | 0.03 | 0.015 | 0.25 | |||
Gr3 | Bal | / | / | / | / | / | 0.30 | 0.08 | 0.05 | 0.015 | 0.35 | |||
Gr5 | Bal | 5.5~6.75 | 3.5~4.5 | / | / | / | 0.30 | 0.08 | 0.05 | 0.015 | 0.20 | |||
Gr5ELI | Bal | 5.5~6.5 | 3.5~4.5 | / | / | / | 0.25 | 0.08 | 0.03 | 0.0120 | 0.13 | |||
2.Mechanical property
Grade | Tensile strength Rm/Mpa | Yield strength Rp0.2/Mpa | Elongation A% | Reduce of area Z% |
Gr1 | >=240 | >=140 | >=24 | >=30 |
Gr2 | >=400 | >=275 | >=20 | >=30 |
Gr3 | >=500 | >=380 | >=18 | >=30 |
Gr5 | >=895 | >=825 | >=10 | >=25 |
Gr5ELI | >=830 | >=760 | >=10 | >=15 |
3.Quality control
*Advanced detection equipment
Ultrasonic flaw detection,infra-red appratus,turbine detector
The turbine detector probes surface flaws above 3mm and 100% ultrasonic flaw detection checks inner defects
below 3mm,they can guarantee titanium bars quality both inner and outer;infrared detection apparatus measures the whole bardiameter from bottom to top,in a word,we try our best to ensure the product quality better through primary test ,middle test, final test.
* Test report with 3rd party: BaoTi Test Center Physical and Chemical Test Report for Consigned Text,; Physics and Chemistry Inspection Center for Western metal Materials Co,.Ltd.
4.Other products we can produce
Titanium Medical Bars/Rod
Titanium Medical Plates/sheets
Titanium Welding wire
Titanium Standard Parts
Titanium Foil
Zirconium Crucible
Zirconium Bar
Molybdenum Products
We provide you with high quality, competitive price and satisfactory after--sale service.
We are looking forward to your inquiry.