工業的用途のためのASTM B265チタン薄板
Product Information
Product | 工業的用途のためのASTM B265チタン薄板 |
Grade | Gr. 1, 2, 3, 4, 5 |
Specification | |
Standard | ASTM F67, ASTM F136, ISO 5832-2, ISO 5832-3, ASTM B265 |
Application | Orthopedic implants 1. Chemical industry 2. Petrochemical industry 3. Machining field,Automobile field,etc 4. Desalination of sea water 5. Textile printing and dyeing |
Package | Plywood export case |
Delivery time | 7-15 days |
Technology | Hot rolling, cold rolling, annealed |
Surface | Pickling, Sandblasting, Polishing |
Test | With mill test, accept the third party test. |
Chemical Composition--Medical
Commercial Pure Medical Titanium Materials
Grade | Ti | Chemical composition | |||||||||||
Major composition | Impurity(=<%) | Residual elements | |||||||||||
Al | V | Sn | Mo | Pa | Fe | C | N | H | O | Single | Total | ||
Gr1 | Bal | / | / | / | / | / | 0.20 | 0.08 | 0.03 | 0.015 | 0.18 | 0.10 | 0.40 |
Gr2 | Bal | / | / | / | / | / | 0.30 | 0.08 | 0.03 | 0.015 | 0.25 | 0.10 | 0.40 |
Gr3 | Bal | / | / | / | / | / | 0.30 | 0.08 | 0.05 | 0.015 | 0.35 | 0.10 | 0.40 |
Gr4 | Bal | / | / | / | / | / | 0.50 | 0.08 | 0.05 | 0.015 | 0.40 | 0.10 | 0.40 |
Titanium Alloy Materials
Grade | Ti | Chemical composition | ||||||||
Major composition | Impurity(=<%) | Residual elements | ||||||||
Al | V | Fe | C | N | H | O | Single | Total | ||
TI6AL4VELI | Bal | 5.5~6.5 | 3.5~4.5 | 0.25 | 0.08 | 0.05 | 0.012 | 0.13 | 0.10 | 0.40 |
Mechanical Properties--Medical
Material | Condition | Thickness mm | Mechanical Property | ||
Tensile strength Rm/Mpa | Yield strength Rp0.2/Mpa | Elongation A% | |||
Gr1 | M | <25 | Min 240 | Min 170 | Min 24 |
Gr2 | Min 345 | Min 275 | Min 20 | ||
Gr3 | Min 450 | Min 380 | Min 18 | ||
Gr4 | Min 550 | Min 483 | Min 15 |
Material | Condition | Thickness mm | Mechanical Property | |||
Tensile strength Rm/Mpa | Yield strength Rp0.2/Mpa | Elongation A% | Reduction of area Z/% | |||
TI6AL4VELI | M | <25 | Min 862 | Min 793 | Min 10 | Min 25 |
Please feel free to contact us for more imformation.