製品情報
原産地: 中国(本土) | 銘柄: 華中 | モデル番号: Hz-qj202 |
仕様
1.非- 腐食性と非- 吸湿性2.ポスト治療を必要としませんろう付け接合部分の
Hz-qj202フラックスは、 白色微粉末から成るの混合物をfluroroaluminate塩類がカリウムは非腐食性と非吸湿性である。 the flux of the highest quality and consistency is produced under stringent process tolerances and a variety of quality control procedures by us。
The flux has a melting point ポイント of 558・度; c to 620・度; c、 この真下を共晶al-si系ろう付け合金の温度。 サイズにあるそのthe particle1um50μmの範囲に。
During the brazing process the flux dissolves the oxide layer on aluminum and allow the filler me-tal to flow freely into the joints by capillary action。 after cooling、 the flux residue remains on the surface as a thin adherent film and is noncorrosive and nonhygroscopic。 the flux does not require post brazing treatment of the joint area。
説明
chemical composition
k ( %)
28-31
al ( %)
16から18
f ( %)
49-53
fe ( %)
max
0.03
ca ( %)
max
0.2
Application tests
brazing test
color test
particles test
black residue test
si (%)
max
0.05
physical properties
外観
White powder
Density(20・度; c)
2.8g/cm3
Bulk density
400600g/l
Melting point(・度; c)
558-620 ・度; c
パッキング
Paper druMs with 私Nner pe bags。
25kg net weight。
Solubility in water
Nearly insoluble
Particle size( 50%)
2~10 um
アプリケーション |
自動車: radiator、 oil cooler、 condenser、 evaporator、 heater core、 Accumulator assemblies。 |
家庭用: kitchen pans and pots、 kettle、 coffee machines、 iron、 clothes ドライヤー。 |
Brazing process
1. cleaning : the surface to be brazed must be pre- cleaned to achieve a water Wettable surface。
2. flux application : usually as a water based slurry。 typical the slurry Concentration is in the range of 3% to 25%。
3. drying : To achieve a successfully brazed component it is essential that all Water is removed from the flux coating。 a drying process is carried out at Approximately 180・度; c - 250・度; c。
4.the process requirement of brazing furnace:
Inert atmosphere - usually nitrogen as this is the cheapest。
Dewpoint less than minus 40・度; c。
Operating temperature range of 558-620・度; c、 coinciding with the melting point の The cladding。
Rate of heating of the component greater than 20・度; c per minute。