原産地: 中国(本土)	銘柄: PENGCHENG	モデル番号: PC-EV1253
タイプ: 絶縁の製陶術	材料: ほう素の窒化物	色: 白い
形: ガスケット	粒度: 0.5-1.5	比誘電率108Hz: 4.0
絶縁破壊電圧(Kv/mm): 2-3	B+N: 99.5%	酸素分: <0>
炭素分: <0>	Mohの硬度: 2	熱拡張の係数: 0.49

包装

包装: 袋およびカートンをvacuumize

仕様

絶縁の製陶術のほう素の窒化物の陶磁器のよいガスケットのほう素の窒化物のガスケットのbn.のよい安定性SGS

白い絶縁のほう素の窒化物の製陶術

 

Prepared using vacuum hot sintered pressing hexagonal boron nitride and composite materials for its excellent high temperature performance、 slag and molten me-tal corrosion resistance、 high thermal conductivity and high electrical insulation、 and ease of processing performance  (available general machining processing methods and products derived from high dimensional accuracy)の in the amorphous alloy  production as thin strip nozzle has been widely used . The company's amorphous ultrafine crystalline  (nanocrystalline)の with a boron nitride nozzle strip are using in production process for the formulation of different products can be used for Fe-based、 FeNi-based and Co-based amorphous soft magnetic alloy and Ni-Cu-based brazing amorphous alloys and other products. 

 

Main technical characteristics:  

1. Boron nitride material structure tightness、 the bulk density ≥ 2.2g/cm3、 compressive strength ≥ 300MPa、 apparent porosity ≤ 0.5%;  

 non-cracking 2. Organization delicateの smooth wear-resistant  non-delamination;  

3. Rating of temperature above 1600 degrees;  

4. Thermal expansion coefficient little. 

For spraying molten me-tal alloy. Through to the moving cooling substrate のthen rapidly solidified and solidification me-tal strip to produce rapidly solidified me-tal ligature.