| 原産地: | 中国(本土) | 銘柄: | navilla | モデル番号: | 076 | 原産地: | 中国 | ブランド: | navilla | タイプ: | コンクリートレンガ | 技術: | 蒸気の硬化した | 構造: | 固体 |
包装
| 包装: | ・パレットカートン |
仕様
exterior decorative lightweight brick veneer wall Ideal for both outside and inside residential,commercial and landscape decoration1.Advantages:
1.Light weight with beautiful surface texture |
2 Good abrasion resistance,wear-resistant |
3.High strength and zero drying shrinkage |
4.Can stand strong impact and various climate change |
5.Durable,high quality, permanent ,colorfast inorganic pigments. |
6.Waterproof and frostproof to avoid discoloration over long service span. |
7.EN, ASTM certificate can be provided. |
Large quantity ,various colors of navilla thin brick veneer panels are available.Sincerely hope we can have a win-win cooperation with you. |
2.Package
| Mode | Quantity/Caton ( m2 ,m) | Quantity/ 20 feet container(m2,m) | Weight/ctn (kg) | Size 0f ctn L×W×H(cm) | Cartons/ PLT | Cartons/ 20 feet container | PLT |
| flat | 1 | 1040 | 17 | 57×22×14.5 | 48/56 | 1040 | 10+10 |
| (corner) | 4.6 | 4784 | 18 | 57×22×14.5 | 48/56 | 1040 | 10+10 |
3.product test:
Wall brick | Test Method | Results | |||
Flexural strength(Mpa) | EN14167-2:2005 | 3.8 | |||
Compression strength(Mpa) | EN14167-15:2005 | 14.9 | |||
Water absorption(%) | EN14167-1:2005 | 5.4(non-waterproof), 1.9(waterproof) | |||
Freeze/Thaw Resistance (%) | Lost rate of Flexural strength | EN14167-5:2005 | 28.9 | ||
Lost rate the mass | EN14167-5:2005 | 0.2 | |||
Freezing and Thawing cycle
| ASTM C67-03a | Weight loss after 50 freezing and thawing cycles |
results
| requirement | |
0.08% | ≤3% | ||||
Remark(EN) | The lost rate of flexural strength is the ratio calculated from the flexural strength after and before 25frost cycles.The strength after frost is 2.7Mpa While 3.8Mpa before it. | The lost rate of the mass is the ratio calculated from the mass determined after and before 50 frost cycles.the mass after the frost is 178.45g while 178.80before it. | |||
Remark(ASTM) | After 50freezing and thawing cycles,the samples have not been inspected cracking and breakage. | ||||