原産地: 中国(本土) | 形: レンガ | 材料: ムライト |
SiO2成分(%): 29-45% | Al2O3成分(%): 37-68% |
包装
包装: carton/pallet |
仕様
1鉄、アルカリや不純物、良好な高温特性、還元雰囲気へのエネルギー良好な耐性に低い内容。 2均質構造、軽量、高破砕強度、優れた絶縁特性、冷却加熱サイクル中に炉本体の下位蓄熱ので省エネ。 3高強度、高温下での良好な安定性及び体積耐熱衝撃性。
1 Lower content in iron, alkaline and impurities, goodhigh temperature properties, energy good resistance to reduction atmosphere.
2 Homogeneous structure, light weight, high crushingstrength, good insulating properties, energy saving because lower heat storagein the furnace body during cooling-heating cycles.
3 High strength, good volume stability and thermal shockresistance under high temperature.
4 Less size tolerance due to grinding and shaping aftersintering, this meets the requirement of construction.
Brand
Item | ||||
Al2O3(%)min | 37 | 50 | 60 | 68 |
Fe2O3(%)max | 1.0 | 1.0 | 0.7 | 0.5 |
SiO2(%)max | 45 | 43 | 36 | 29 |
Safty Application Temp.(°C)max | 1260 | 1430 | 1540 | 1650 |
Bulk Density(g/cm3) | 0.5 | 0.8 | 0.95 | 1.05 |
Bending strength(Mpa)min | 0.7 | 1.1 | 1.6 | 2.0 |
Crush strength(Mpa)min | 1.0 | 2.0 | 2.3 | 2.7 |
RLC(%)max | 1230°C×24h 0.3 | 1400°C×24h 0.4 | 1510°C×24h 0.5 | 1600°C×24h 0.6 |
Reversible thermal expansion at1090°C(%) max |
0.5 |
0.6 |
0.8 |
0.8 |
Thermal conductivity (w/m.k)max 400°C 600°C 800°C 1000°C |
0.15 0.17 0.19 0.24 |
0.28 0.31 0.33 0.35 |
0.33 0.36 0.39 0.42 |
0.41 0.43 0.45 0.48 |